ResinLab EP1300 Epoxy Encapsulant Black 50 mL Cartridge

Part number: EP1300 BLACK 50ML
ResinLab EP1300 Epoxy Encapsulant Black 50 mL Cartridge
Quantity Price
1 $1,908.80 ($47.72 each) 1908.800000000 CAD New Limited Availability EP1300 BLACK 50ML
2 $1,772.40 ($44.31 each) 1772.400000000 CAD New Limited Availability EP1300 BLACK 50ML
3+ $1,661.20 ($41.53 each) 1661.200000000 CAD New Limited Availability EP1300 BLACK 50ML
Sold as a pack (40/pk).
Usually Ships in 2-3 Business Weeks. Subject to prior sales. Non-returnable product. Canceled orders may incur a fee at the supplier’s discretion. Product not sold online in Quebec.
  • J Haz Class 8

ResinLab EP1300 Black is a two component, room temperature or heat curing, unfilled epoxy encapsulant that is used for small to medium castings. It is electronic grade, free flowing, and has good wetting and air release. It is resistant to bases, acids, water, and most organic solvents. 50 mL Cartridge.

<p>ResinLab EP1300 Black is a two component, room temperature or heat curing, unfilled epoxy encapsulant that is used for small to medium castings. It is electronic grade, free flowing, and has good wetting and air release. It is resistant to bases, acids, water, and most organic solvents. 50 mL Cartridge.</p>
Typical Use: Electronic grade epoxy encapsulant for small to medium sized castings.
Chemical Composition: Epoxy
Color: Black
Components: 2 part
Cure System: Room Temperature/Heat
Cure Time: 30min @ 100 °C; 1h @ 80 °C; 4h @ 50 °C
Dielectric Strength: 850 V/mil
Elongation: 11%
Flash Point: Part A: 252 °C; Part B: >101 °C
Hardness: 80 D
Mix Ratio: 1:1 by volume; 1.21:1 by weight
Service Temperature: -40 to 150 °C
Shear Strength: 1,300
Specific Gravity: Part A: 1.16; Part B: 0.96; Mixed: 1.06
Tack Free Time: 3 to 4h
Tensile Strength: 4,500 psi
Thermal Conductivity: &lt;0.2 W/mK
Viscosity: Part A: 15,000; Part B: 7,000; Mixed: 8,000
Volume Resistivity: 3.3 x 10^15 ohm-cm

 