ResinLab EP1238 Epoxy Adhesive Off-White 400 mL Cartridge

Part number: EP1238 400ML
ResinLab EP1238 Epoxy Adhesive Off-White 400 mL Cartridge
Quantity Price
1 $1,171.68 ($195.28 each) 1171.680000000 CAD New Limited Availability EP1238 400ML
2 $902.16 ($150.36 each) 902.160000000 CAD New Limited Availability EP1238 400ML
3+ $837.72 ($139.62 each) 837.720000000 CAD New Limited Availability EP1238 400ML
Sold as a pack (6/pk).
Usually Ships in 2-3 Business Weeks. Subject to prior sales. Non-returnable product. Canceled orders may incur a fee at the supplier’s discretion. Product not sold online in Quebec.
  • J Haz Class 8

ResinLab EP1238 Black is a two component, room temperature and heat curing, epoxy/acrylic adhesive that is used for bonding plastics and metals. It offers controlled flow, good wetting, semi-rigid material and resistance to salt solutions, water, vibrations, impact, organic and inorganic solvents. 400 mL Cartridge.

<p>ResinLab EP1238 Black is a two component, room temperature and heat curing, epoxy/acrylic adhesive that is used for bonding plastics and metals. It offers controlled flow, good wetting, semi-rigid material and resistance to salt solutions, water, vibrations, impact, organic and inorganic solvents. 400 mL Cartridge.</p>
Typical Use: Designed for bonding metals and plastics.
Chemical Composition: Acrylic/epoxy hybrid
Color: Off-White
Components: 2 part
Cure System: Room Temperature/Heat
Cure Time: 24h @ 25 °C; 2h @ 65 °C
Dielectric Strength: 888 V/mil
Elongation: 25% to 45% @ break
Flash Point: Part A: 249 °C; Part B: >93 °C
Hardness: 80 D
Mix Ratio: 2:1 by volume; 100:47 by weight
Peel Strength: 25 pli
Service Temperature: -40 to 150 °C
Shear Strength: 4,000
Specific Gravity: Mixed: 1.13
Tensile Strength: 8,500 psi
Thermal Conductivity: 0.18 W/mK
Viscosity: Mixed: 65,000
Volume Resistivity: 1.6 x 10^15 ohm-cm
Working Time: 20min

 