ResinLab EP1238 Epoxy Adhesive Black 50 mL Cartridge

Part number: EP1238 BLACK 50ML
ResinLab EP1238 Epoxy Adhesive Black 50 mL Cartridge
Quantity Price
1 $4,426.80 ($36.89 each) 4426.800000000 CAD New Limited Availability EP1238 BLACK 50ML
2 $4,110.00 ($34.25 each) 4110.000000000 CAD New Limited Availability EP1238 BLACK 50ML
3+ $3,852.00 ($32.10 each) 3852.000000000 CAD New Limited Availability EP1238 BLACK 50ML
Sold as a pack (120/pk).
Usually Ships in 3-4 Business Weeks. Subject to prior sales. Non-returnable product. Canceled orders may incur a fee at the supplier's discretion. Product not sold online in Quebec.
  • J Haz Class 8

ResinLab EP1238 Black is a two component, room temperature and heat curing, epoxy/acrylic adhesive that is used for bonding plastics and metals. It offers controlled flow, good wetting, semi-rigid material, and resistance to salt solutions, water, vibrations, impact, organic and inorganic solvents. 50 mL Cartridge.

ResinLab EP1238 Black is a two component, room temperature and heat curing, epoxy/acrylic adhesive that is used for bonding plastics and metals. It offers controlled flow, good wetting, semi-rigid material, and resistance to salt solutions, water, vibrations, impact, organic and inorganic solvents. 50 mL Cartridge.
Typical Use: Designed for bonding metals and plastics.
Chemical Composition: Acrylic/epoxy hybrid
Color: Black
Components: 2 part
Cure System: Room Temperature/Heat
Cure Time: 6 to 12h @ 25 °C; 2h @ 65 °C; 30min @ 100 °C
Dielectric Strength: 888 V/mil
Elongation: 3% to 4% @ break
Flash Point: Part A: 249 °C; Part B: >93 °C
Hardness: 80 D
Mix Ratio: 2:1 by volume; 2.12:1 by weight
Peel Strength: 25 pli
Service Temperature: -40 to 150 °C
Shear Strength: 280 to 4,600
Specific Gravity: Mixed: 1.13
Tensile Strength: 8,500 psi
Thermal Conductivity: <0.2 W/mK
Viscosity: Mixed: 47,000
Volume Resistivity: 2.12 x 10^16 ohm-cm

 